Txoj kab uas hla | Tensile Load | Tensile zog | Shear zog | E-modulus (GPa) |
6 | 38 | 1300 |
≥150 |
≥55 |
12 | 125 | 1200 | ||
16 | 185 | 1000 | ||
20 | 255 | 900 | ||
25 | 410 | 850 |
Ntau txoj kab uas hla raws li kev xav tau
Lub npe | BFRP Cov | |
Qhov ceev (g / cm³) | 1.9 ~ 2.1 | |
Tensile zog (MPa) | ≥750 | |
Tensile M-modulus (MPa) | ≥4.0 | |
Elongation (%) | ≥1.8 | |
Kub expansion coefficient (×10+/℃) | Ntev | 9 ~ 12 |
| Kab rov tav | 21-22 : kuv |
E Alkali Resistance (Kev tuav ruaj khov %) | ≥85 | |
Sib nqus susceptibility (4 π x 10 SI) | ≤5 |